| TYPE |
GRADE |
ALLOY COMPONENTS |
PHYSICAL MECHANISM CHARACTERISTICS |
APPLICATION |
DENSITY
(g/cm3) |
OIL CONTINED
(Vol%) |
CRUSHING STRENGTH
(kgf/mm2) |
APPARENT HARDNESS
(HB) |
| IRON BASE |
FZ1260 |
Fe-C |
5.7~6.2 |
 18 |
>25 |
50~100 |
ELECTRIC FAN,WASHING
MACHINE,MIXER,HOUSEHOLD APPLIANCE PART;OFFICE FACILITIES AND
METER,ETC |
| FZ1265 |
Fe-C |
6.2~6.6 |
12 |
>30 |
60~100 |
| FZ1360 |
Fe-C-Cu |
5.7~6.3 |
18 |
>35 |
60~110 |
| FZ1365 |
Fe-C-Cu |
6.2~6.6 |
12 |
>40 |
70~120 |
| AFZ1460 |
Fe-Cu |
5.8~6.3 |
18 |
>28 |
50~100 |
| BFZ1460 |
Fe-Cu |
5.8~6.3 |
18 |
>15 |
40~70 |
| COPPER BASE |
FZ2170 |
Cu-Sn-Zn-Pb |
6.6~7.2 |
18 |
>15 |
20~50 |
| FZ2175 |
Cu-Sn-Zn-Pb |
7.2~7.8 |
12 |
>20 |
30~60 |
| |
HIGH
ACCURACY,LOW NOISE,LASTING HIGH SPEED RUNNING MICRO OIL IMPREGNATED
BEARING |
|
| TYPE |
PHYSICAL MECHANISM CHARACTERISTICS |
APPLICATION |
DENSITY
g/cm3 |
NOISE
(RANGE50mm),
dB |
OIL CONTAINED
(VOL)% |
WEAR EXTENT
(3000rpmX
500gX200h),
|
FRICTION COEFFICIENT
(3000rpmX500g) |
CRUSHING STRENGTH
Mpa |
APPARENT HARDNESS(300g/30s)
MHv |
LIFETIME
(3000rpm
X500g),h |
| COPPER BASE |
6.5 - 7.5 |
< 20 |
> 18 |
< 12 |
< 0.4 |
> 216 |
60 ~ 90 |
> 2000 |
ALL KINDS OF MICRO
MOTORS |
| IRON AND COPPER BASE |
6.0 - 6.8 |
< 20 |
> 18 |
< 12 |
< 0.25 |
> 216 |
60 ~ 100 |
> 2000 |
| IRON BASE |
5.9 - 6.6 |
< 20 |
> 18 |
< 12 |
< 0.30 |
> 245 |
60 ~ 100 |
> 2000 |
| TYPE |
ALLOY COMPONENTS |
PHYSICAL MECHANISM
CHARACTERISTICS |
APPLICATION |
TENSION STRENGHTH
(kgf/mm2) |
ELONGATION
(%) |
IMPACT TOUGHNESS
(kgf/mm2) |
DENSITY
(g/cm3) |
APPARENT HARDNESS
(HB) |
| SINTERED IRON |
Fe-C |
10 |
3.0 |
0.5 |
6.2~70 |
40 |
MOTOR
BIKE,VEHICLE,ELECTRIC TOOL,HOUSEHOLD APPLIANCE,ETC. |
| SINTERED LOW-CARBON
STEEL |
Fe-C |
10 |
1.5 |
0.5 |
6.2~70 |
50 |
| SINTERED MIDCARBON
STEEL |
Fe-C |
15 |
1.0 |
0.5 |
6.2~70 |
60 |
| SINTERED HIGH-CARBON
STEEL |
Fe-C |
20 |
0.5 |
0.3 |
6.2~70 |
70 |
| SINTERED COPPERSTEEL |
Fe-C-Cu |
25 |
0.5 |
0.3 |
6.2~70 |
90 |
|
|